High strength machinable glass-ceramics

ABSTRACT

In one aspect the invention is directed to a machinable glass-ceramic having a high degree of crystallinity (greater than 50 Vol. %), high mechanical strength (MOR&gt;150 MPa) In accordance with the invention, the machinable glass-ceramics described herein consists essentially of, in weight percent, 35-55% SiO 2 , 6-18% Al 2 O 3 , 12-27% MgO, 3-12% F, 5-25% SrO, 0-20% BaO and 1-7% K 2 O. The machinable glass-ceramics of the invention have a dielectric constant of &lt;8 (typically being in the range of 6-8) at 25° C. and 1 KHz; a loss tangent of &lt;0.002 at 25° C. and 1 MHz; a CTE in the range of 80-120×10 −7 /° C. in the temperature range of 25-300° C.; a Poisson&#39;s ration of approximately 0.25; and a porosity of 0%.

PRIORITY

This application claims the priority of U.S. Provisional Application No. 61/074,815 filed Jun. 23, 2008 in the name of George H. Beall.

FIELD

The invention is directed to high strength machinable glass-ceramic materials.

BACKGROUND

Mica is classified as a phyllosilicate; its basic structural feature is a composite sheet in which a layer of octahedrally-coordinated cations is sandwiched between two identical layers of linked (Si,Al)O₄ tetrahedra. The general formula of the mica structure can be found in Dana's New Mineralogy, R. V. Gaines et al., eds. (John Wiley & Sons, New York 1997), pages 1444-1446 and the structure can be written as:

A₀₋₅R₂₋₃T₄O₁₀X₂,

where:

A=a large monovalent or bivalent ion (e.g. Na⁺, K⁺, Rb⁺, Cs⁻, Ca²⁺, Sr²⁺, Ba²⁺), or a partial vacancy (partial vacancy denoted by subscript “0”),

R=an octahedrally-coordinated cation (e.g. Li⁺, Mg²⁺, Fe²⁺, Mn²⁺, Zn²⁺, Al³⁺, Fe³⁺, Mn³⁺, V³⁺),

T=a tetrahedrally-coordinated cation (predominantly Si⁴⁺, with Al³⁺ and B³⁺), and

X=is an anion (predominantly OH⁻ in minerals, but F⁻ in glass-ceramics. X may also be partially O²⁻.)

Micas are extremely common in rocks, and numerous classification systems exist for them. In glass-ceramics, micas are typically classified as alkaline (containing alkali ions) and non-alkaline (containing no monovalent ions), and as trisilicic (where T₄ in the formula above is (Si₃Al)) and tetrasilicic (Si₄). These compositional parameters can be varied to produce desired properties in a glass-ceramic.

Machinable mica glass-ceramics based on mica crystal phases were originally disclosed in the art more than thirty years ago [e.g. U.S. Pat. Nos. 3,689,296, 3,732,087, 3,839,055, and 3,756,838], and Table 1 below shows general formulas for trisilicic, tetrasilicic and non-alkali glass-ceramics having mica structures, the alkali-containing glass-ceramics being included in the trisilicic and tetrasilicic categories. These materials have found numerous uses based on their unusual capability of being machinable to high tolerances using conventional high speed metal-working tools. By suitably tailoring their compositions and nucleation and crystallization temperatures, a wide range of microstructures can be obtained, including the “house-of-cards” microstructure of relatively large mica crystals with high two-dimensional aspect ratios, which most enhances the inherent machinability of the materials (see W. Höland and G. Beall, Glass Ceramic Technology (Amer. Ceramic Soc., Westerville, Ohio, 2002), pages 7-9 and 236-241. Additionally, one can refer to U.S. Pat. No. 2.920,971 (Stookey), the basic patent in the field of glass-ceramics, which provides an extensive study of the practical aspects and theoretical considerations that must be understood in the manufacture of such articles as well as a discussion of the crystallization. More recent disclosures of machinable glass-ceramics (largely directed to glass-ceramics for dental applications) include PCT International Publication No. WO 2004/071979 A2 and U.S. Pat. Nos. 6,645,285, 6,375,729, 6,645,285, 4,652,312, 5,246,889 and 4,431,420. The foregoing machinable mica glass-ceramics typically have an inherent white color. For certain applications, however, especially for consumer-oriented products or dental applications (hued to match existing teeth), a colored machinable glass-ceramic is desired.

While existing machinable glass-ceramic have many valuable properties, improvement are still highly desirable, particularly with regard to strength and fracture toughness. The present invention is directed to a machinable glass-ceramming having improved characteristics, including high strength and high fracture toughness.

TABLE 1 General Types of mica structures in glass-ceramics (prior art) Trisilicic Tetrasilicic Non-alkali Wt % mica GCs GC mica GC SiO₂ 25-60  45-75 30-65  Al₂O₃ 5-25 0-5 5-26 B₂O₃ 5-15 0 MgO 5-25  8-30 10-35  F 4-20  3-15 4-12 K₂O See below  2-20 Li₂O 0-7  0-5 R₂O 2-20 See below ZrO₂ 0-7 SrO 5-25 BaO 0-25 Where The sum of Al₂O₃ + B₂O₃ = 15-35% Na₂O = 0-5 The sum of MgO + Li₂O = 6-25% R₂O = alkali oxides: K₂O = 0-15% Na₂O = 0-15% Rb₂O = 0-15% Cs₂O = 0-20%

SUMMARY

In one aspect the invention is directed to a high strength machinable glass-ceramic having a high degree of crystallinity (greater than 50 Vol. % in one embodiment; greater than 60 Vol. % in another embodiment; and greater than 80 Vol. % in a further embodiment; the remainder percentage being the glass phase), high mechanical strength (MOR>150 MPa, MOR=Modulus of Rupture), In accordance with the invention, the machinable glass-ceramics described herein consist essentially of, in weight percent on an oxide basis (except fluorine which is simply F and is not an oxide), 35-55% SiO₂, 6-18% Al₂O₃, 12-27% MgO, 3-12% F, 6-25% SrO, 0-20% BaO and 1-7% K₂O. In an additional embodiment the composition of the invention consists essentially of 35-55% SiO₂, 6-18% Al₂O₃, 12-27% MgO, 3-12% F, 6-25% SrO, 5-20% BaO and 1-5% K₂O (to reduce swelling and lower the dielectric constant K). In another embodiment the composition consists essentially of, in weight percent, 40-50% SiO₂, 8-12% Al₂O₃, 14-22% MgO, 5-10% F, 8-18%% SrO, 0-20% BaO and 2-5% K₂O.

In another embodiment the machinable glass-ceramics of the invention may also be colored to an appropriate colored using colorants known in the art, Examples, without limitation, of such colorants include Co₃O₄, CoO (blue-violet); NiO (grey-brown); Cr₂O₃ (green-brown); CuO (blue-green); FeO, Fe₂O₃ (green-brown); NiS (grey); CdS (yellow). The colorants are added in an amount in the range of >0 wt % to ≦3 wt %, except that when the colorant is iron the iron is present in an amount of >0 wt % to ≦20 wt %. The colorants are added in the form of metal oxides and/or sulfides. Black machinable glass-ceramics can be made by adding FeO+Fe₂O₃ in an amount in the range of 2-20 wt %, preferably in the range of 7-20 wt %. Typically when colorants are added, they replace part of the SiO₂, Al₂O₃, MgO and SrO when SrO is greater than 5 wt %.

In a further embodiment the invention is directed to a colored machinable glass ceramics having a color other than black, a preferred composition consisting essentially of 35-55% SiO₂, 6-18% Al₂O₃, 12-27% MgO, 3-12% F, 6-25% SrO, 0-20% BaO and 1-7% K₂O and colorant in the range of >0 wt % to ≦3 wt %. In a further embodiment, the invention is directed to a black colored, machinable glass-ceramic consisting essentially of 35-55% SiO₂, 6-18% Al₂O₃, 12-27% MgO, 3-12% F, 6-25% SrO, 0-20% BaO and 1-7% K₂O, and 7-20% FeO+Fe₂O₃.

DETAILED DESCRIPTION

When a composition herein is given a range of 0-X wt %, this range refers to the amount of material added to a batch and excludes contaminant levels of the same material. As those skilled in the art know, metals, for example, sodium and iron, are frequently found at contaminant levels in batched glass and glass-ceramic products. Consequently, it is to be understood that in those cases where a material is not specifically added to a batch, added, any such material that may be present in an analyzed sample of the final glass-ceramic material is contaminant material. Except for iron oxides, where contaminant levels are typically around the 0.03 wt % (300 ppm) level, contaminant levels are less than 0.005wt % (50 ppm). The term “consistently essentially of” is to be understood as not including contaminant levels of any material.

The invention is directed to machinable glass-ceramics containing the predominant phase fluormica which is believed composed of a solid solution between SrMg₆Al₂Si₆O₂₀F₄ and KMg₃AlSi₃O₁₀F₂, and where Ba may partially replace Sr. These machinable glass-ceramics, show a high crystallinity and high mechanical strength (MOR>150 MPa). For example, slabs of rough dimensions 4″×1″×½″ were thrown with force onto the floor without breakage, indicative of high strength and high fracture toughness. In contrast, commercially available glass-ceramics such as Macor™ broke in such experiments. The high strength of the glass-ceramics of the invention is believe attributable to the high crystallinity of interlocking tabular fluormica crystals and the strong bonding present in this fluormica, where a predominance of divalent cations, such as strontium (or strontium combined with barium), predominates in the mica interlayer. This increased interlayer bonding strength is likely also responsible for the increased hardness, while the interlocking tabular crystallinity allows machinability. The machinable glass-ceramics of the invention have a dielectric constant of <8 (typically being in the range of 6-8) at 25° C. and 1 KHz; a loss tangent of <0.002 at 25° C. and 1 MHz; a CTE in the range of 80-120×10⁻⁷/° C. in the temperature range of 25-300° C.; and a Poisson's ratio of approximately 0.25 and a porosity of 0%.

The machinable glass-ceramics can be formed by methods known in the art, for example, U.S. Pat. No. 3,756,838. In the broadest terms, the present invention consists of melting a batch for a glass consisting essentially of, by weight percent on an oxide basis, 33-55% SiO₂, 6-18% Al₂O₃, 12-27% MgO, 5025% SrO, 0_(—)20% BaO, 1-7% K₂O and 3-12% F. It is critical to the invention to have significant SrO present both as a good glass-enhancing oxide and to allow Sr²⁺ to act as a strongly-bonded interlayer cation. Consequently, all composition in accordance with the invention contain at least 5 wt % SrO. Additionally, at least 1 wt % K₂O must be present to prevent undesirable water-swelling effects that are known to occur with pure Sr-mica glass-ceramics. After melting, the resulting glass is cooled below the transformation range, formed into the desired shaped, and subsequently heat treated at a temperature in the range of 800-1200° C., preferably at a temperature in the range of 1000-1150° C., for a time sufficient to secure crystallization in situ. [The transformation temperature is defined as the temperature at which the liquid melt has been formed into an amorphous solid; that temperature commonly considered as lying between the strain point and annealing point of a glass.] Those skilled in the art appreciate that in as much as crystallization in situ is both time and temperature dependent, the higher the temperature the shorter will be the time required for crystallization. When the temperatures are at the upper end of the range the time will be shorter (for example, 1-2 hours or less) and when they are at the lower end of the range they will be longer (for example, 20-40 hours).

Colored machinable glass-ceramics in accordance with the invention can also be made by addition of an appropriate colorant to the glass batch prior to melting and ceramming. Examples, without limitation, of such colorants include Co₃O₄, CoO (blue-violet); NiO (grey-brown); Cr₂O₃ (green-brown); CuO (blue-green); FeO, Fe₂O₃ (green-brown when added at ≦3 wt %); NiS (grey); and CdS (yellow). The colorants are added in an amount in the range of >0 wt % to ≦3 wt %, except that when the desired color is black and the colorant is iron, the iron is present in an amount in the range of >3 wt % to ≦20 wt %. The colorants are added in the form of metal oxides and/or sulfides. At levels of ≦3 wt % the colorants are simply added to the glass batch prior to melting.

Black machinable glass-ceramics can be made by adding FeO+Fe₂O₃ in an amount in the range of >3-20 wt %, preferably in the range of 7-15 wt %, to the glass batch prior to melting. The iron colorant(s) may simply be added to the batch or can be a replacement for some of the magnesia and/or alumina present in the batch. However, when iron is added to produce a black machinable glass-ceramic, the SrO level must be maintained at least 5 wt % and the K₂O level must be at least 1 wt %.

In one embodiment, for colored machinable glass ceramics having a color other than black, a preferred composition consists essentially of 36-55% SiO₂, 7-17% Al₂O₃, 13-27% MgO, 3-12% F, 6-25% SrO, 0-20% BaO, 1-7% K₂O and >0 wt % to ≦3 wt % colorant.

In a further embodiment, the invention is directed to a black colored, machinable glass-ceramic consisting essentially of 35-55% SiO₂, 7-13% Al₂O₃, 13-20% MgO, 3-12% F, 6-20% SrO, 0-20% BaO and 1-7% K₂O, and 7-20% FeO+Fe₂O₃.

The machinable glass-ceramics of the invention have greater than 50 Vol. % crystalline phase and less than 50 Vol. % glass (non-crystalline) phase. In one embodiment glass-ceramics have a greater than 60 Vol. % crystalline phase and less than 40 Vol. % glass phase. In a further embodiment the glass-ceramics have a greater than 75 Vol. % crystalline phase and less than 25 Vol. % glass phase. In addition to the predominant crystalline phase the glass-ceramic can contain minor amounts of additional crystalline phases, for example without limitation, a non-alkali phase like cordierite. The predominant crystalline phase is trisilicic where 2.5<T>3.5 and can be written as a formula A₀₋₅R₂₋₃T_(2.5-3.5)O₁₀X₂ where A, R, T and X are as described above.

The machinable glass-ceramics of the invention have a dielectric constant of <8 (typically being in the range of 6-8) at 25° C. and 1 KHz; a loss tangent of <0.002 at 25° C. and 1 MHz; a CTE in the range of 80-120×10⁻⁷/° C. in the temperature range of 25-300° C.; a Poisson's ration of approximately 0.25; and a porosity of 0%.

Table 1 compares the broadest composition of the glass-ceramic disclosed herein (“Claimed”) and those of two commercially machinable glasses, Macor™ (Corning Incorporated, Corning, N.Y.) and Vitronit™ Vitron Spezialwerkstoffe GmbH, Thuringen, Germany). Machinable glass-ceramics MC-LD and MC-HD (Marketech, Port Townsend, Wash.) are identified as being alkaline or alkaline earth zirconium phosphate NaZr₂P₃O₁₂ or BaZr₄P₆O₂₄, and do not contain silica, alumina, magnesia, potassium oxide or fluorine as far as can be determined. Other machinable glass-ceramics whose analyzed composition or formula could not be identified are Micaver® (St. Gobain, Nemours Cedex, France) and Photoveel (available from Scientific Instrument Services, Inc, Ringeos, N.Y.).

TABLE 1 Composition, wt. % SiO₂ Al₂O₃ MgO SrO BaO K₂O F Other Claimed 33-55 6-18 12-27 6-25 0-20 1-7 3-12 — Macor* 46 16 17 — — 10 4 B = 7 Vitronit* 46 29 12 — —  5 4 Na = 4 *= reported composition by manufacturer

Various modifications and variations can be made to the materials, methods, and articles described herein. Other aspects of the materials, methods, and articles described herein will be apparent from consideration of the specification and practice of the materials, methods, and articles disclosed herein. It is intended that the specification and examples be considered as exemplary. 

1. A machinable glass-ceramic consisting essentially of, in weight percent on a oxide basis, 35-55% SiO₂, 6-18% Al₂O₃, 12-27% MgO, 5-25% SrO, 0-20% BaO, 1-7% K₂O and 3-12% F, and, when present, >0% to ≦3% colorant, except that when a colorant is used to produce a black glass-ceramic the colorant is present in the range of >3% to 20%; wherein said glass ceramic has greater than 50 Vol. % crystalline phase and less than 50 Vol. % glass phase, and a mechanical strength greater than 150 MPa.
 2. The machinable glass-ceramic according to claim 1, wherein aid glass ceramic has greater than 60 Vol. % crystalline phase and less than 40 Vol. % glass phase.
 3. The machinable glass-ceramic according to claim 1, wherein aid glass ceramic has greater than 80 Vol. % crystalline phase and less than 20 Vol. % glass phase
 4. The machinable glass-ceramic according to claim 1, wherein the colorant used to produce a black machinable glass-ceramic is FeO, F₂O₃ in an amount in the range of >3% to 20% by weight.
 5. The machinable glass ceramic according to claim 4, wherein the amount of colorant is in the range of 7-15% by weight.
 6. The machinable glass-ceramic according to claim 1, wherein the glass-ceramic has a porosity of 0%, a dielectric constant of in the range of 6-8 at 25° C. and 1 KHz; a loss tangent of <0.002 at 25° C. and 1 MHz; a CTE in the range of 80-120×10⁻⁷/° C. in the temperature range of 25-300° C.; and a Poisson's ratio of approximately 0.25.
 7. A machinable glass-ceramic consisting essentially of, by weight percent on a oxide basis, 35-55% SiO₂, 7-17% Al₂O₃, 13-27% MgO, 3-12% F, 6-25% SrO, 0-20% BaO, 1-7% K₂O and, when present, a colorant in the range of >0 wt % to ≦3 wt %; and wherein said glass ceramic has greater than 60 Vol. % crystalline phase and less than 40 Vol. % glass phase.
 8. The machinable glass-ceramic according to claim 7, wherein aid glass ceramic has greater than 80 Vol. % crystalline phase and less than 20 Vol. % glass phase.
 9. The machinable glass-ceramic according to claim 5, wherein the glass-ceramic has a porosity of 0%, a dielectric constant of in the range of 6-8 at 25° C. and 1 KHz; a loss tangent of <0.002 at 25° C. and 1 MHz; a CTE in the range of 80-120×10⁻⁷/° C. in the temperature range of 25-300° C.; and a Poisson's ratio of approximately 0.25.
 10. A black colored machinable glass-ceramic consisting essentially of 35-55% SiO₂, 7-13% Al₂O₃, 13-20% MgO, 3-12% F, 5-20% SrO, 0-20% BaO and 1-7% K₂O, and 7-20% FeO+Fe₂O₃.
 11. The machinable glass-ceramic according to claim 10, wherein the glass-ceramic has a porosity of 0%, a dielectric constant in the range of 6-8 at 25° C. and 1 KHz; a loss tangent of <0.002 at 25° C. and 1 MHz; a CTE in the range of 80-120×10⁻⁷/° C. in the temperature range of 25-300° C.; and a Poisson's ratio of approximately 0.25.
 12. The glass-ceramic according to claim 10, wherein the glass-ceramic has a mechanical strength greater than 150 MPa.
 13. The machinable glass-ceramic according to claim 10, wherein aid glass-ceramic has greater than 60 Vol. % crystalline phase and less than 40 Vol. % glass phase.
 14. The machinable glass-ceramic according to claim 10, wherein aid glass-ceramic has greater than 80 Vol. % crystalline phase and less than 20 Vol. % glass phase.
 15. A machinable glass-ceramic consisting essentially of, by weight percent on a oxide basis, 35-55% SiO₂, 6-18% Al₂O₃, 12-27% MgO, 3-12% F, 6-25% SrO, 5-20% BaO and 1-5% K₂O.
 16. The machinable glass-ceramic according to claim 15, wherein the glass-ceramic has a porosity of 0%, a dielectric constant of in the range of 6-8 at 25° C. and 1 KHz; a loss tangent of <0.002 at 25° C. and 1 MHz; a CTE in the range of 80-120×10⁻⁷/° C. in the temperature range of 25-300° C.; and a Poisson's ratio of approximately 0.25.
 17. The glass-ceramic according to claim 15, wherein the glass-ceramic has a mechanical strength greater than 150 MPa.
 18. The machinable glass-ceramic according to claim 15, wherein aid glass-ceramic has greater than 60 Vol. % crystalline phase and less than 40 Vol. % glass phase.
 19. The machinable glass-ceramic according to claim 15, wherein aid glass-ceramic has greater than 80 Vol. % crystalline phase and less than 20 Vol. % glass phase. 